It's most likely brass. And they must have been brazed from the factory. The brazed joint will melt at a much lower temp than the steel so if you were to weld new it I'd expect it to distort slightly. shouldn't be too much of a problem if you weld it in bursts just to avoid heating up the material around the weld too much.